EHLA: Corrosion and Wear Protection with Lasers

With EHLA, metal protective layers can be applied with extreme high-speed. (Source: V. Lannert, Fh. ILT)

Protecting components against corrosion and wear is no simple matter. Standard processes such as hard chrome plating, thermal spraying and deposition welding have drawbacks. Up to now, laser material deposition has been used only in specific applications. With extreme high-speed laser material deposition, or EHLA, researchers at Fraunhofer ILT in Aachen and RWTH Aachen University have developed and patented an alternative process to overcome shortcomings of the conventional processes in the areas of coating technology and repair. “We can now use EHLA to apply thin layers in the range of a tenth of a millimeter over large surfaces within a short time, while being resource-efficient and economical,” Dr. Andres Gasser, group manager at Fraunhofer ILT, summarizes.

One of the most common processes for the application of corrosion and wear protective coatings is hard chrome plating. However, this consumes a lot of energy. In addition, chromium(VI) harms the environment – which is why, from September 2017, it can only be used with specific authorization. EHLA now offers companies an economical alternative. Its chemical-free application makes the process very environmentally friendly. The resulting layer is metallurgically bonded to the base material and, unlike hard chrome layers, does not delaminate. While hard chrome plating layers have pores and cracks, layers produced using EHLA are non-porous and, thus, offer more efficient long-term protection.

Thermal spraying, too, has disadvantages. This process consumes a lot of material and gas because only about half of the material used ends up coating the component surface. In addition, the resulting layers bond only weakly to the substrate. Due to their porosity, it is necessary to apply several layers, each roughly 25 to 50 µm thick, on top of each other. In comparison, the new EHLA process uses about ninety percent of the material, making it far more resource efficient and economical. Not only are the individual layers non-porous, they also bond firmly to the substrate.

Extreme high-speed laser material deposition (EHLA): protection against wear and corrosion, repair and additive manufacturing – all with only one system technology. (Source: Fh. ILT)

Deposition welding processes are used to produce high-quality and firmly bonded coatings. With conventional processes such as tungsten inert gas (TIG) welding or plasma powder deposition, however, the layers of 2 to 3 mm are often far too thick and, as a result, too much material is used. Laser material deposition already allows for far thinner layers – between 0.5 and 1 mm, but is too slow for large components, which is why it has only been used for specific applications so far. A further drawback of the process is that it requires a certain melt pool size to create a defect-free layer: The component is locally melted, while a powder nozzle directs a powdery additive into the melt pool. Dr. Gasser explains the key element of the new process: “With EHLA, the laser melts the powder particles while they are above the melt pool.” Since this means that drops of liquid material fall into the weld pool instead of solid powder particles, the layer becomes more homogenous. In addition, less base material needs to be melted: Instead of up to a millimeter, now only a few micrometers suffice.

As a result, the component can be coated 100 to 250 times faster than with conventional laser material deposition, with minimal heating of the substrate. Thus, EHLA facilitates the coating of heat-sensitive components, which was impossible due to excessively high heat input up to now. Also, the new process can be used for completely new material combinations such as coatings on aluminum base alloy or cast iron.

Left to right: Laudator Prof. Hartmut Hoffmann, TU Munich, Gerhard Backes, RWTH Aachen University, Dr. Andres Gasser, Fraunhofer ILT, Prof. Reimund Neugebauer, President Fraunhofer Society, Thomas Schopphoven, Fraunhofer ILT. (Source: Fh. ILT)

In close cooperation with Acunity from Aachen, Germany, which is a spin-off of the Fraunhofer ILT, the Dutch company Hornet Laser Cladding will deliver the first EHLA system to China soon. It shall be used for research purposes and industrial applications at the Advanced Manufacture Technology Center of China Academy of Machinery Science & Technology CAMTC in Beijing.

At the Fraunhofer General Assembly Meeting, held on May 30 in Dresden, Germany, Dr. Andres Gasser, Thomas Schopphoven and Gerhard Maria Backes received the Joseph von Fraunhofer prize, which carries a reward of 50,000 euros, in recognition of their work. (Source: Fh. ILT)

Reference: Th. Schopphoven, A. Gasser & G. Backes: EHLA: Extreme High-Speed Laser Material Deposition – Economical and effective protection against corrosion and wear, Laser Tech. J., in press